Chemical composition % of steel C22E (1.1151): EN 10083-2-2006

Cr + Mo + Ni = max 0.63

C	Si	Mn	Ni	P	S	Cr	Mo
0.17 - 0.24	max 0.4	0.4 - 0.7	max 0.4	max 0.03	max 0.035	max 0.4	max 0.1

New opportunities for buyers!
Post free buying requirement of steel C22E (1.1151)

Mechanical properties of steel C22E (1.1151)

Nominal thickness (mm):	to 16	16 - 100

Rm - Tensile strength (MPa) (+N)	430	410

Nominal thickness (mm):	0.3 - 3

Rm - Tensile strength (MPa) (+A)	500

Nominal thickness (mm):	0.3 - 3

Rm - Tensile strength (MPa) (+CR)	900

Nominal thickness (mm):	to 8	8 - 20	20 - 50	50 - 80

Rm - Tensile strength (MPa) (+QT)	500	470	440	420

Nominal thickness (mm):	to 8	8 - 20	20 - 50	50 - 80

ReH - Minimum yield strength (MPa) (+QT)	340	290	270	260

Nominal thickness(mm):	to 16	16 - 100

Re - Upper yield strength or R_p0.2 - 0.2% proof strength (MPa) (+N)	240	210

Nominal thickness(mm):	0.3 - 3

R_p0.2 0.2% proof strength (MPa) (+A)	400


KV - Impact energy (J) (+QT)	+20° 40-50


KV - Impact energy (J) transverse, (+QT)	+20° 27-32

Nominal thickness (mm):	0.3 - 3

A - Min. elongation Lo = 80 mm (%) (+A)	22

Nominal thickness (mm):	to 8	8 - 20	20 - 50	50 - 80

A - Min. elongation at fracture (%) longitud., (+QT)	20	22	22	22

Nominal thickness (mm):	to 16	16 - 100

A - Min. elongation Lo = 5,65 √ So (%) (+N)	24	25

Vickers hardness ( HV): (+CR	265
Vickers hardness ( HV): (+A)	155
Brinell hardness (HB): (+A)	156

Properties of steel C22E (1.1151)

Weldability: Easily weldable.
Hardenability: Extremely low hardenability, used above all for pieces of small section and when deformations due to water-quenching are allowed.

Equivalent grades of steel C22E (1.1151)Warning! Only for reference

EU
EN

USA
-

Germany
DIN,WNr

Japan
JIS

France
AFNOR

England
BS

Italy
UNI

Russia
GOST

C22E

1020

Ck22

S20C

XC18

070M20

CS22

C25